Notes

HOME>Notes

Note on j-sen clip available

Thank you for using our clip.
Our clip We will be using a polycarbonate resin.
Polycarbonate has good transparency, strength also has a strong advantage, but please note that there is a risk of damage at the following situation.

1.The use of the thing a thick

Our clip it becomes basically utilizing the principle of leverage structure.
It takes a considerable amount of weight on the combination part of the parts at the time of opening and closing.
Possible that sandwich the thing with the thickness of up to a certain extent, if that is continue to use in the same situation, there is a risk of shape change, please note that there is a risk in the worst case, lead to corruption.
If it is available to those with a thick, we recommend more a small clip from the shape of large (5,6,21L type) clip of shape.
If you can tell in advance for your intended use, we will propose a more suitable product.

2.chemical resistance

Polycarbonate resin is there is not good disadvantage in regard to chemical durability.
In particular alkaline agent, tend to deteriorate in a solvent, epoxy adhesives has been unsuitable.
Please refer to because I was allowed to specify the chemical resistance in Exhibit.
However, since you do not mean to say that all is certainly true if you have any questions, please contact us.

3.hazardous substances

Polycarbonate that you are using in our clip, we have cleared both the reference value "bisphenol A", "formaldehyde".
Please tell us if you go in so we will offer a copy of both the test results.

polycarbonate material versus chemical resistance list

For resin
Operating temperature limit -130 ℃ ~ 135 ℃
Solvent temperature 140 ℃ ~ 150 ℃
Autoclave (121 ℃ · 15 minutes, 1 bar) Yes
Density (specific gravity) 1.2 / cm3
Water-absorbing property <0.35%
Collimated refractive index 1.586nD
General chemical resistance
Acetylene good
Cyclohexane good
Cyclohexanol good
Diethylene glycol good
Glauber’s salt good
Ethylene glycol good
Formic acid good
Hexen alcohol good
Isobutyl alcohol good
Isopropyl alcohol good
Potassium chloride good
Potassium cyanide good
Potassium nitrate good
Potassium sulfate good
Propyl alcohole good
Sodium bicarbonate good
Sodium bisulfate good
Sodium nitrate good
Sodium phosphate good
Sodium sulfite good
Sulfurous acid good
Dibenzyl ether Not recommended
Dibuthylether Not recommended
Diethyle ether Not recommended
Hexane Not recommended
Hydrobromic acid Not recommended
Hydrochloric acid Not recommended
Nitric acid Not recommended
Propyl acetate Not recommended
Acetic acid no good
Aceton no good
Benzene no good
Bromine no good
Chloroacetone no good
Chloroform no good
Chlorosulfonicacid no good
Chlorotoluene no good
Cyclohexanone no good
Dichlorobenzene no good
Ethyl chloride no good
Fluorobenzene no good
Methyl acetate no good
Methyl alcohol no good
Methyl chloride no good
フェノール(Phenol) no good
Potassium hydroxide no good
Sodium peroxide no good
Sulfuric no good
Tetorachloroethane no good
Tetrahydrofuran no good
Toluene no good
trichloroethylene no good
Xylene no good

This table is quoted from the polymer dictionary. These are all the test data, it does not guarantee the accuracy for use conditions, such as concentration and temperature is different.